Stereolithography - more commonly referred to as SLA – is one of the most popular and widespread techniques in the world of additive manufacturing. It works by using a high-powered laser to harden liquid resin that is contained in a reservoir to create the desired 3D shape. In a nutshell, this process converts photosensitive liquid into 3D solid plastics in a layer-by-layer fashion using a low-power laser and photo polymerization.

Every standard SLA 3D printer is generally composed of four primary sections:

• A tank filled with the liquid photopolymer: The liquid resin is usually a clear and liquid plastic.
• A perforated platform immersed in a tank: The platform is lowered into the tank and can move up and down according to the printing process.
• A high-powered, ultraviolet laser
• A computer interface, which manages both the platform and the laser movements.

Process of Stereolithography

1. Software

As is the case for many rapid manufacturing processes, the first step consists of designing a 3D model through CAD software. The resulting CAD files are digitalized representations of the desired object.

If they are not automatically generated as such, the CAD files must be converted into STL files. Standard tessellation language (STL), or “standard triangle language”, is a file format native to the stereolithographic software created by the Abert Consulting Group specifically for 3D Systems back in 1987. STL files describe the surface geometry of the 3D object, neglecting other common CAD model attributes, such as colour and texture.

The pre-printer step is to feed an STL file into a 3D slicer software, such as Cura. Such platforms are responsible for generating G-code, the native language of 3D printers.

2. SLA 3D Printing

When the process starts, the laser “draws” the first layer of the print into the photosensitive resin. Wherever the laser hits, the liquid solidifies. The laser is directed to the appropriate coordinates by a computer-controlled mirror.

At this point, it’s worth mentioning that most desktop SLA printers work upside-down. That is, the laser is pointed up to the build platform, which starts low and is incrementally raised.

After the first layer, the platform is raised according to the layer thickness (typically about 0.1 mm) and the additional resin is allowed to flow below the already-printed portion. The laser then solidifies the next cross-section, and the process is repeated until the whole part is complete. The resin that is not touched by the laser remains in the vat and can be reused.

3. Post-Processing

After finishing the material polymerization, the platform rises out of the tank and the excess resin is drained. At the end of the process, the model is removed from the platform, washed of excess resin, and then placed in a UV oven for final curing. Post-print curing enables objects to reach the highest possible strength and become more stable.

Advantages

• SLA is one of the most precise 3D printing techniques on the market.
• Prototypes can be created with extremely high quality, with finely detailed features (thin walls, sharp corners, etc…) and complex geometrical shapes. Layer thicknesses can be made as low as 25 $\mu m$, with minimum feature sizes between 50 and 250 $\mu m$.
• SLA provides the tightest dimensional tolerances of any rapid prototyping or additive manufacturing technology: $\pm$ 0.005″ (0.127 mm) for the first inch, and an additional 0.002″ for each additional inch.
• Print surfaces are smooth.
• Build volumes can be as high as 50$\times$50 $\times$60 $cm^3$ without sacrificing precision.

Disadvantages

• Printing tends to take a long time.
• Steep slopes and overhangs require support structures during the building process. Such parts may potentially collapse during printing or curing phases.
• Resins are comparatively fragile and therefore not suitable for functional prototypes or mechanical testing.
• SLA offers limited material and color choice, usually offering black, white, grey and clear material. Resins are oftentimes proprietary and therefore cannot be easily exchanged between printers from different brands.
• SLA printing costs are comparatively high (e.g. machine,materials, lab environment).